Thermal cycles effects on interlaminar shear strength (ILSS) and impact behaviour of carbon/PEI composites


Sinmazcelik T., Arici A. A.

JOURNAL OF MATERIALS SCIENCE, cilt.41, ss.1233-1241, 2006 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 41
  • Basım Tarihi: 2006
  • Doi Numarası: 10.1007/s10853-005-3661-5
  • Dergi Adı: JOURNAL OF MATERIALS SCIENCE
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.1233-1241
  • Kocaeli Üniversitesi Adresli: Evet

Özet

In this paper, the effect of thermal cycle on the interlaminate shear strength (ILSS) and impact behaviour of unidirectional carbon fibre reinforced polyetherimide (PEI) matrix composites were studied. Samples were subjected to 100 thermal cycles (by immersing from boiling water (100 degrees C) to ice water (0 degrees C). The effects of thermal cycles were characterized by short beam shear and instrumented impact testers. Also Fractographic investigations were done using a scanning electron microscope (SEM). It is observed that the plastic deformations at the fibre/matrix and interlaminar interface as well as residual stresses lower the ILSS and flexural modulus of the material proportional with the number of thermal cycles. Up to the first 20 thermal cycles the material shows a brittle fracture with lower fracture energy, but after the 20th thermal cycles it is possible to observe that the material fractures with higher fracture energy at longer fracture time. A remarkable difference in the fracture morphology between the thermal cycled and un-treated materials has been observed. It is found that thermal cycles strictly affect the fracture morphology. (c) 2006 Springer Science + Business Media, Inc.