POLYMER COMPOSITES, cilt.1, sa.1, ss.1-9, 2024 (SCI-Expanded)
Drilling glass fiber reinforced polymer matrix (GFRP) composites typically causes burrs, splintering, and microcracks within the GFRP structure, as well as delamination, fiber pull-out, and thermal degradation of the polymer matrix. Designing and manufacturing molded-hole GFRP components, as opposed to drilling, has recently been proposed as a promising method for overcoming the issues associated with drilling, for which there is limited research. Specifically, the mechanical response of molded-hole GFRP has not been fully addressed in the literature. In the present study, molded and drilled GFRP composites with epoxy matrix were fabricated by hand lay-up, and then the samples were analyzed utilizing experimental and numerical analysis techniques. Stress and strain analyses of GFRP samples were performed in Ansys Transient Structural Analysis. Although the fiber orientations of the layer geometries [0°/90°] and 3D models were the same, an additional layer was defined in the direction of the fiber orientation [45°/−45°] of molded-hole composites to simulate the fiber accumulation effect. Experimental findings revealed that the flexural strength of molded composites was 12% greater than that of drilled composites. According to the numerical analysis, 98.7% proximity was achieved between the experimental and numerical results. Thus, the present study has provided numerical modeling to understand the flexural strength of molded composites for the first time, which will contribute to the increased use of molded composites in numerous applications in the fields of aerospace, automotive, and marine.