Effect of the cBN Content and Sintering Temperature on the Transverse Rupture Strength and Hardness of cBN/Diamond Cutting Tools

Kir D., ISLAK S., ÇELİK H., ÇELİK E.

SCIENCE OF SINTERING, cilt.44, sa.2, ss.235-243, 2012 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 44 Sayı: 2
  • Basım Tarihi: 2012
  • Doi Numarası: 10.2298/sos1202235k
  • Dergi Adı: SCIENCE OF SINTERING
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.235-243
  • Kocaeli Üniversitesi Adresli: Evet

Özet

The aim of this work was to investigate the effect of cBN content and sintering temperature on the transverse rupture strength (TRS) of cBN/diamond cutting tools produced by hot pressing. The segments containing different cBN content were manufactured under 35 MPa pressure at 600, 650 and 700 degrees C with a 3 minutes sintering time. The TRS of segments were determined using three-point bending test. Microstructure and phase composition of fracture surface of segments were determined by scanning electron microscopy (SEM), and X-ray diffraction (XRD) analysis. The obtained results show that the TRS of the segments with cBN were higher than that of the segments with diamond.