Microstructural, mechanical and corrosion behavior of UNS S31803/Hastelloy C-276 dissimilar metal welds

ATAPEK Ş. H., TÜMER M., Çelikkol E., KISASÖZ A., Kerimak M. Z.

CIRP Journal of Manufacturing Science and Technology, cilt.40, ss.129-141, 2023 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 40
  • Basım Tarihi: 2023
  • Doi Numarası: 10.1016/j.cirpj.2022.11.008
  • Dergi Adı: CIRP Journal of Manufacturing Science and Technology
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Compendex, INSPEC
  • Sayfa Sayıları: ss.129-141
  • Anahtar Kelimeler: Characterization, Dissimilar weld, GTAW, Hastelloy C-276, UNS S31803
  • Kocaeli Üniversitesi Adresli: Evet

Özet

In this study, UNS S31803 duplex stainless steel and Hastelloy C-276 nickel-based superalloy were joined by gas tungsten arc welding (GTAW) process. Nickel based ERNiCr-3 and ERNiCrMo-3 filler metals with different chemical compositions were used for joining the dissimilar metals. Metallurgical structures of the joint parts were determined by microstructural characterization studies. In mechanical characterization, both hardness and impact toughness were measured. Corrosion behavior of the welds were investigated by potentiodynamic polarization tests in 3.5% NaCl solution. Characterization studies showed that (i) weld metals had a dendritic/cellular solidification structure which changed due to thermal effects in all passes from the surface to the root, (ii) depending on the chemical composition of the filler metal, Nb-rich carbides and Laves phase were formed in the weld metal, (iii) the amount of Mo affected toughness, hardness, and corrosion resistance.