Recrystallization textures and microstructures of Al-0.3% Cu alloy after deformation to high strains
36th Riso International Symposium on Materials Science, Riso, Danimarka, 7 - 11 Eylül 2015, cilt.89, (Tam Metin Bildiri)
- Yayın Türü: Bildiri / Tam Metin Bildiri
- Cilt numarası: 89
- Doi Numarası: 10.1088/1757-899x/89/1/012032
- Basıldığı Şehir: Riso
- Basıldığı Ülke: Danimarka
- Açık Arşiv Koleksiyonu: AVESİS Açık Erişim Koleksiyonu
- Kocaeli Üniversitesi Adresli: Hayır
Özet
An Al-0.3% Cu alloy was deformed to high strains by cold rolling. The as-deformed samples were annealed at different temperatures until complete recrystallization. The cold rolling textures were determined by X-ray diffraction while the recrystallization textures and microstructures were characterized by electron backscatter diffraction. It was found that the rolling texture was characterized by a strong Brass component. After complete recrystallization Goss and Cube textures were developed. The effects of deformation strain and annealing temperature on the recrystallization textures are discussed.